Avtor: Slowfly, Kraj: Ljubljana Objavljeno: Pet Dec 22, 2006 6:47 pm    Naslov sporočila:  
----------------------------------------------------------------------------
Evo, našel sem tisti priročnik za galvaniziranje. Opisani so postopki niklanja, kromanja, bakrenja, cinkanja, kadmiranja ter medeninjenja.
Za bakrenje sta opisana dva postopka. V kisli in v bazični kopeli.
- kisla kopel: bakrimo lahko medenino, predhodno niklane predmete, ter seveda baker.
Sestavine elektrolita za 1l kopeli:
- 200 g modre galice, raztopimo v tolikšni količini vode , da dobimo 995 ml raztopine
-30 g kemično čiste H2SO4 (koncentrirane), previdno dolivamo v prejšnjo raztopino

Bakrimo pri napetosti 2-3 V in toku 1- 2 A/dm2
Anode - plošče iz čistega bakra
Kad za galvaniziranje plastična ali steklena
Temperatura 18 - 22 °C, ne pod 15°C

Površina je mesnato-rožnata, brez kovinskega sjaja, debelina nanosa ni problematična.


Alkalna kopel:bakrimo lahko svinec, železo, cink, kositer in zlitine teh kovin.
Za 1 l kopeli potrebujemo:
- 80 g bakrovega ciankalija
- 2 g ciankalija
- 2 salmijakove soli
- 10 g kuhinjske soli (NaCl)

Druga varianta za pripravo iste kopeli je:
I.- 25 g modre galice raztopimo v 0,5 l vode
II.- 25 g nevtralnega natrijevega sulfita ter 17 g sode raztopimo v 0,25 l vode
III.- 200 g ciankalija raztopimo v 0,1 l vode

Raztopina II se vliva v raztopino I, ter dobro premeša, pri tem nastane gosta zelena vsedlina. Na to se naliva raztopina III, ki to vsedlino raztopi. Mešanica raztopin se dolije do 1 l.

Gostota kopeli je 10° Be´
Napetost 2 - 3,5 V
Gostota toka 0,3 - 0,5 A
Anode plošče iz elektrolitskega bakra.
Kad plastična ali steklena
Temperatura enko kot pri kisli kopeli

Omejitev pri debelini nanosa, bakrimo lahko največ 15 minut naenkrat. Za debelejše nanose moramo površino, ki je bila nanešena v postopku galvanizacije , mehansko obdelati, krtačenje z medeninasto krtačo- neprimerno ra reliefno površino.


Če je kdo zainteresiran, lahko dobi kopijo priročnika, krije stroške kopiranja.

lp

Nazadnje urejal/a Slowfly Pet Dec 22, 2006 7:37 pm; skupaj popravljeno 1 krat

---

Avtor: Slowfly, Kraj: Ljubljana Objavljeno: Pet Dec 22, 2006 7:09 pm    Naslov sporočila:  
----------------------------------------------------------------------------
Za doseganje sjajne površine bakrenih predmetov, uporabimo naslednji postopek.
Pripravimo si kopel iz:
- 0,1 l dušikove kisline
- 0,1 l žveplene H2SO4 kisline
- 1 g saj
- 1 g NaCl

Žvepleno kislino previdno dolivamo v dušikovo kislino, dodamo saje, ter na koncu še sol. V to raztopino potapljamo bakrene predmete za kratek čas.

Bolje se obnese, tudi hitreje deluje kombinacija dveh kopeli.

Kopel I.: 0,1 l dušikove kisline + 1 cm3 solne kisline- HCl
Kopel II.: 0,1 l dušikove kisline + 0,1 l žveplene kisline + 2 cm3 solne kisline + 1 g saj.

Predmet za nekaj sekund pomočimo v kopel I. , nato ga dobro speremo z vodo, nato ga za 1-2 sekundi pomočimo v kopel II. , ter ponovno dobro speremo pod tekočo vodo.
Temperatura kopeli med 20 in 30 °C.

lp

---

Avtor: igo,  Objavljeno: Sob Dec 23, 2006 1:29 am    Naslov sporočila:  
----------------------------------------------------------------------------
Nekaj zgoraj omenjenih kemikalij je precej strupenih .

Se ne bi dalo cina spraviti v luknjico s pomočjo kapilarnega efekta?
Takorekoč stvar geometrije luknje in razlike površinskih napetosti cina ter materiala ploščice.
No, ja, frekvenčne lastnosti povezave bi bile verjetno obupne , a do nekaj MHz (da pokrije splošno uporabljene kontrolerčke) bi šlo.
Lep pozdrav,
Igor

---

Avtor: Slowfly, Kraj: Ljubljana Objavljeno: Sob Dec 23, 2006 2:23 am    Naslov sporočila:  
----------------------------------------------------------------------------
Saj teh strupenih kemikalij ni treba ravno piti! Za nas v glavnem pride v poštev kisla kopel, torej raznih ciankalijev ne potrebujemo (razen mogoče za kakšno taščo)
Tudi ženske znajo biti hudo strupene, pa se vseeno ukvarjamo z njimi.
Je pa tale priročnik, kot sem že omenil hudičevo star, izdan je bil malo pred drugo svetovno vojno.
Pa da ne bo kdo mislil, da dandanašnji v galvanah uporabljajo kaj bolj zdravju in okolju prijaznega.

---

Avtor: cero, Kraj: vipava Objavljeno: Sob Dec 23, 2006 4:25 pm    Naslov sporočila:  
----------------------------------------------------------------------------
tukaj je še par drugih načrtov mogoče bodo komu v pomoč:

6. ELECTRO GOLD PLATING - NEW METHOD
Take 100 grams of laminated gold, mixed with 20 grams of hydrochloric
acid; 10 grams of nitric acid; the liquid thus composed is placed over a
moderate fire, and stirred constantly until the gold passes into the state
of chlorine; it is then allowed to cool. A second liquid is formed by
dissolving 60 grams of cyanide of potassium in 80 grams of distilled
waters; the two liquids are mixed together in a decanter and stirred for
20 minutes, and then filtered. Finally 100 grams of whiting, dry and
sifted, are mixed with 5 grams of pulverised supertartrate of potass; this
new powder is dissolved in a portion of the above described liquid, in
sufficient quantity to form a paste of the proper consistency to be spread
with a pencil on the article or part to be gilded. The superabundant
powder is then removed by washing and the article is beautifully gilded
with a heavy or light coat, according to the quantity of paste used. Grams
belong to French weights, four grams are a little more than one drachm.

ELECTRO SILVERING - NEW METHOD
10 grams of nitrate of silver are dissolved in 50 grams of distilled
water; then 25 grams of cyanide of potassium in 50 grams of distilled
water; the two liquids are mixed in a decanter, and stirred for 10
minutes; it is then filtered. Finally, 100 grams of sifted whiting are
mixed with 10 grams of pulverised supertartrate of potass and one gram of
mercury. This powder and dissolving liquid are used in the same manner as
in the above method of gold plating. These excellent methods of silvering
and gilding were discovered in June 1860, by the great French chemist
Baldooshong of Paris France. It is far superior to any other method ever
discovered, and will eventually take the place of all.

8. ELECTRO GOLD PLATING - USUAL METHOD
Take a $2 50c. piece of gold, and put it into a mixture of 1 ounce of
nitric and 4 ounces of muriatic acids, (glass vessels only are to be used
in this work,) when it is all cut dissolve 1/2 an ounce of sulphate of
potash in one pint of pure rain water, and mix the gold solution, stirring
well; then let stand and the gold will be thrown down; then pour off the
acid fluid, and wash the gold in two or three waters, or until no acid is
tasted by touching the tongue to the gold. Now dissolve one ounce of
cyanuret of potassium in one pint of pure rain water, to which add the
gold, and it is ready to use. Clear the article to be plated from all dirt
and grease with whiting and a good brush; if there are cracks it may be
necessary to put the article in a solution of caustic potash. At all
events every particle of dirt and grease must be removed; then suspend the
article in the cyanuret of gold solution, with a small strip of zinc cut
about the width of a common knitting needle, hooking the top over a stick
which will reach across the top of the vessel or bottle holding the
solution. If the zinc is too large the deposit will be made so fast that
it will scale off. The slower the plating goes on the better, and this is
arranged by the size if the zinc used. When not using the plating fluid
keep it well corked and it is always ready to use, bearing in mind that it
is poison as arsenic, and must be put high out of the way of children, and
labelled poison, although you need have no fear using it; yet accidents
might arise it its nature were not known.

9. ELECTRO SILVERING - USUAL METHOD
This is done every way the same as gold plating (using coin) except that
rock salt is used instead of the cyanuret of potassium to hold the silver
in solution for use, and when it is of the proper strength of salt it has
a thick curdy appearance, or you can add salt until the silver will
deposit on the article to be plated, which is all that is required. No
hesitation need be felt in trying these receipts, as they are obtained
from a genuine source, and are in every day use.

10. GOLD PLATING FLUID
Warm six ounces of pure rain water, and dissolve in it 2 ounces of cyanide
of potassium, then add a 1/4 ounce oxide of gold; the solution will at
first be yellowish, but will soon subside to white; then half fill a
bottle with whiting, fill it up with this solution and shake it well; you
may now take a piece of old cotton, wet it with the solution, rub it well
over brass, copper, &c., and it is nicely washed with gold.

11. SILVER PLATING FLUID
Dissolve one ounce of nitrate of silver, in crystal, in 12 ounces of soft
water; then dissolve in the water two ounces of cyanuret of potash; shake
the whole together and let it stand until it becomes clear. Have ready
some 1/2 ounce vials, and fill them half full of whiting, then fill up the
bottles and it is ready for use. The whiting does not increase the coating
powder - it only helps to clear the articles and save the silver fluid by
half filling the bottles. The above quantity of materials will cost about
$1.62c., so that the fluid will be about 3 cents a bottle. It is used in
the same way as the gold plating fluid.

LP cero

---

Avtor: piroman, Kraj: Ljubljana Objavljeno: Sob Dec 23, 2006 8:56 pm    Naslov sporočila:  
----------------------------------------------------------------------------
Zanimivo! Precej uporabno bi bilo kositranje, brez elektrike, seveda. Kemikalije je težko dobit v majhnih količinah ali po spodobnih cenah. Upam, da jih kje staknem...

---

Avtor: piroman, Kraj: Ljubljana Objavljeno: Sob Dec 30, 2006 7:22 pm    Naslov sporočila:  
----------------------------------------------------------------------------
Tako, moja galvana je po praznični prekinitvi danes spet aktivna

Darko, tvojo PTFE ploščico mi je danes uspelo pobakriti. Sem imel kar nekaj problemov, ker je raztopino težko prepričati, da bi dobro omočila teflon. No, 0,35mm luknje so se skoraj bolj pobakrile, kot velike...

V sredo ti vrnem ploščice. Za poskušino pa en foto 0,35mm luknje skozi moj mikroskop. Nastavek za fotoaparat sem nastružil sam in seveda "pozabil" počrnit v notranjosti, zato (tudi) neenakomerna osvetlitev, da o neostrini ne govorim

---

Avtor: VolkD, Kraj: Divača (Kačiče) Objavljeno: Pet Jan 05, 2007 1:35 pm    Naslov sporočila:  
----------------------------------------------------------------------------
Ne bodi preveč kritičen. Slika je dobra!

Ploščoice sem dobil - hvala. Mislim, da so stvari kar uporabne.
Teflon je sicer res trši oreh, a metalizacija v luknji je precej bolj obstojna kot pa na robu, tako, da s tem nebi smelo bit problemov.
Menim, da je že postopek kakršen je sedaj popolnoma uporaben za domačo rabo.


Se bom potrudil z mikroskopom, takoj ko uspem "zaplenit" fotoaparat sinu.

---

Avtor: jur, Kraj: [color=zelena]Ljubljana[/color] Objavljeno: Pet Jan 05, 2007 2:27 pm    Naslov sporočila:  
----------------------------------------------------------------------------
Od zgoraj naštetih kemikalij za metalizacijo je najbolj učinkovita mešanica kalijevega cianida in solne kisline. Učinkovito je do smrti.

Jur

---

Avtor: piroman, Kraj: Ljubljana Objavljeno: Pet Jan 05, 2007 4:21 pm    Naslov sporočila:  
----------------------------------------------------------------------------
VolkD, me veseli, da se ti zdi postopek uporaben. Čez vikend bom malo natuhtal mešanje - imam občutek, da bi se dalo precej učinkoviteje bakriti s tanjši difuzijsko plastjo ob ploščici. Pozna se namreč, da tok hitro pade, čim se raztopina umiri...

Jur, cianidi (ker so soli šibkih kislin) na splošno niso kompatibilni s kislinami. Sicer pa HCN tako hitro zavohaš, ima zelo značilen vonj po grenkih mandljih
Sem svojčas precej delal s heksacianoferati (en kompleks z železom), ker se je dalo na ČB fotografijah črno srebro zamenjati z bakrom...

---

Avtor: .,  Objavljeno: Ned Jan 07, 2007 9:49 pm    Naslov sporočila:  
----------------------------------------------------------------------------
Brisana vsebina odstranjenega uporabnika.

---

Avtor: andrejj, Kraj: 8232 Šentrupert Objavljeno: Pon Jan 08, 2007 9:12 am    Naslov sporočila:  
----------------------------------------------------------------------------
Piroman,si poskusil spajkati?Mene zanima če prime spajke.

---

Avtor: jur, Kraj: [color=zelena]Ljubljana[/color] Objavljeno: Pon Jan 08, 2007 9:35 am    Naslov sporočila:  
----------------------------------------------------------------------------

piroman je napisal/a:

...Jur, cianidi (ker so soli šibkih kislin) na splošno niso kompatibilni s kislinami. Sicer pa HCN tako hitro zavohaš, ima zelo značilen vonj po grenkih mandljih ;)...

Ja, saj vem. Zato pa je bil priložen mrtev smiley... Ko pa HCN pri mešanju kisline in cianida zavohaš, je ponavadi že prepozno.

Jur

---

Avtor: piroman, Kraj: Ljubljana Objavljeno: Pon Jan 08, 2007 10:29 am    Naslov sporočila:  
----------------------------------------------------------------------------
Mare, to, kar jaz uporabljam ni prevodno lepilo ampak moja čorba iz grafita in acetona. Vse skupaj zgleda kot kakšno redko blato, ki ga ženske uporabljajo za... no, za kar pač ženske uporabljajo te stvari Do sedaj se je najbolje izkazala metoda, pri kateri s tanko inox spatulo nabašem grafit v luknje, počakam, da se posuši in potem previdno izpihnem odvečen material.
Sem razmišljal tudi o vakuumu pa žal nimam kake primerne črpalke. Imam sicer eno vodno vakuumsko črpalko ampak je malo prenerodna za uporabo...

Andrejj, lota se zelo lepo. Površina izgleda kot bi bila fino peskana.

---

Avtor: andrejj, Kraj: 8232 Šentrupert Objavljeno: Pon Jan 08, 2007 11:18 am    Naslov sporočila:  
----------------------------------------------------------------------------
Kaj pa če kje dobiš gospodinjsko staro napravo za varenje folije(vrečke).Ki ima notri vakum motor.Tako za poskusiti.Samo če dosti močan.Mogoče pa star sesalec?Pozabil še pripisat.To kar si spajkal,pa me veseli.Da je šlo,to čestitam.

---